Description |
Poliset 9505 is un-promoted Terephthalic type unsaturated polyester resin with low viscosity, high HDT, high corrosion resistance and higher reactivity. Suitable for all forms of closed molding. |
R-401 is specially designed for the production of waterproof board, building materials, automobile parts, water tanks, etc., by the resin transfer molding(RTM) technique. |
R405-O is a low viscosity, fast wet out, low shrink resins suitable for automotive, RV, building materials, etc.. |
Poliset R405-I is an Iso/DCPD resin, with low shrink, fast wet out, yielding a tougher product due to improved resilience. Suitable for RTM and silicone bagging applications. |
Technical Data Sheet |
|
|
|
|
Safety Data Sheet |
|
|
|
|
Application Processes |
Though originally designed as a UL approved it is equally impressive in close mold applications. It demonstrates: • Corrosion resistance with improved toughness • Ideal for high temperature, mildly corrosive service conditions • Can be used for single wall UST (Underground Storage Tank) or the inner and/or outer walls of secondary containment Type I or Type II UST • Superior corrosion and blister resistance • Can replace more expensive vinyl ester resins in some service conditions • Consistent batch-to-batch performance. |
The low viscosity and cure rate suit RTM manufacture for high turn over parts. Includes internal release to ensure good release with no or minimal deposit on mold. |
A superior closed molding resin excellent handling properties, fast turnover and minimal shrinkage. |
Suitable for automotive RV, marine, building and general lamination. Any where fast mold turn around times and low shrinkage is required. |
Benefits |
• High molecular weight, high crosslink density terephthalic polymer • 126°C HDT with good tensile toughness • Good acid, salt solution and polar solvent resistance |
• Fast cure time allowing for fast demold. • Extremely fast wet out. • Good mechanical characteristics. • Fast cure in thin section. • High filler loading possible |
•Excellent wetting properties. •Good mechanical characteristics. •Good resistance to cracking and low shrinkage. •Fast cure in thin section. |
•Excellent wetting properties. •Good mechanical characteristics. •Good resistance to cracking and low shrinkage. •Fast cure in thin section. |
Chemical Structure |
Terephthalic |
Ortho |
Ortho/DCPD |
Iso/DCDP |
Tensile Strength MPa |
60 , Test Method ASTM D638 |
55 |
65-75 |
65 |
Tensile Modulus GPa |
3.3 Test Method ASTM D638 |
3.1 |
N/A |
N/A |
Flexural Strength MPa |
110 Test Method ASTM D790 |
142 |
130 -140 |
120-130 |
Flexural Modulus GPa |
3.6 Test Method ASTM D790 |
3.7 |
3.5 - 4.0 |
3.3 - 3.8 |
Elongation % |
2.1 Test Method ASTM D638 |
1.7 |
2.0-2.5 |
2.5-3.0% |
Heat Distortion Temperature |
126 °C Test Method ASTM D648 |
67 °C |
75 - 80 °C |
75 °C |
Barcol Hardness |
40 Test Method ASTM D2583 |
40+ |
40+ Test Method ASTM D2583 |
40+ Test Method ASTM D2583 |
Viscosity cps@25C |
200 - 300 |
1.8 - 2.5 |
120 - 150 |
120-150 |
Styrene Content |
44% - 50% |
40% - 46% |
37 - 43 |
37% - 43% |
Certificates |
UL1316, UL1746 |
N/A |
N/A |
N/A |
Geltime@1.5% A50 MEKP |
25-35 minute or as specified |
6 - 45 minute or as specified |
4 - 45 minute or as specified |
6 - 45 minute or as specified |
Packaging |
200 litre drum, 1000 litre Schutz |
1,000 litre Schutz, 200 litre Drum, 20 litre Pail |
1,000 litre Schutz, 200 litre Drum |
1,000 litre Schutz, 200 litre Drum |
Storage |
The product should be stored in sealed, original container. Shelf life: Six months below 25℃. Minimum shelf life performance refers to product in the original, unopened, container. Shelf stability is affected by storage conditions. |
The product should be stored in sealed, original container. Shelf life: Six months below 25℃. Minimum shelf life performance refers to product in the original, unopened, container. Shelf stability is affected by storage conditions |
The product should be stored in sealed, original container. Shelf life: Six months below 25℃. Minimum shelf life performance refers to product in the original, unopened, container. Shelf stability is affected by storage conditions |
The product should be stored in sealed, original container. Shelf life: Six months below 25℃. Minimum shelf life performance refers to product in the original, unopened, container. Shelf stability is affected by storage conditions |